A276 S42010 stainless steel round bar quenched in oil

ASTM A276 S42010 stainless steel was manufactured by a heat treatment temperature ranging from 1010℃ to 1010℃.

The typical ASTM A276 S42010 stainless steel type is ASTM A276 S42010 stainless steel. When quenched, ASTM A276 S42010 stainless steel round bars and shapes are recommended being quenched in the oil.

Standard: ASTM A276
UNS designation:
S42010 Grade: martensitic grades
S42010 Quenchchant: oil
S42010 Hardness HRC≥48
S42010 Heat treatment temperature℉(℃)≥1850(1010)

Chemical Composition for ASTM A276 S42010 stainless steel round bars
C 0.15-0.30
S =0.030  
P =0.040
Si =1.00
Mn = 1.00        
Cr 13.5-15.0
Mo 0.40-0.85
Ni 0.35-0.085

Mechanical properties(annealed condition) for ASTM A276 S42010 stainless steel round bars


Grade

Finish

Brinell hardness
(%), max

ASTM A276
S42010

Hot finished

235

Cold finished

255

Notes: When the diameter or thickness over 1 1/2(38.10mm) to 1 3/4(44.45mm), the tensile strength≥860Mpa; yield strength≥690Mpa; elongation≥18%; reduction of area≥45%.

Over the years BEBON has exported ASTM A276 S42010 stainless steel round bars and shapes to many countries all over the world. If you have orders, contact us freely.

With over 8 years experience of supplying A276 S42010 stainless steel round bar to various industries, we have successfully demonstrated our strong commitment to customer satisfaction in terms of quality and reliability of service. Moreover, our own extensive processing capabilities, backed by group resouces, enable us to meet all your needs in A276 S42010 stainless steel round bar.